Plastalloy Physical Properties

 

Aging

 Compressive Yield Strength after 7 days at 200 F, psi  4870
 Moldulus of Elasticity in Compression after 7 days at 200 F, psi  46500
 Modulus of Elasticity in Tension 600 hr. Salt Spray, psi  50000
 Ultimate Tensile Strength after 600 hr. Salt Spray, psi  800
 Ultimate Tensile Strength after 1000 hr. (Weather-O-Meter), psi  750
 Ultimate Elongation after 1000 hr. (Weather-O-Meter), %  4.6
 Ultimate Elongation after 600 hr. Salt Spray, %  8.2
 Modulus of Elasticity in Tension after 1000 hr. (Weather-O-Meter), psi  166000

Mechanical

 Durometer Hardness Shore D  35-60
 Izod Impact Strength, ft-lb/in. of Notch  1.6
 Ultimate Tensile Strength, psi  600
 Elongation at Break, %  3
 Modulus of Elasticity in Tensionn, psi  67000
 Ultimate Shear Strength, psi  1620
 Compression Yield Strength  3700
 Modulus of Elasticity in Compression, psi  30100

Electrical

 Volume Resistivity (X1010) ohm-cm  3.5
 Insulation Resistance (X106) ohm  6.95
 Arc Resistance, sec.  100

Thermal

 Heat Distortian Temp., 264 psi., F  115
 Heat Distortian Temp., 66psi., F  170
 Thermal Conductivity Btu / hr. / F / in.  4.3
 Coefficient of Cubical Thermal Expansion X10-5 per F  5.2
 Maximum Operating Temp., F  300
 Coefficient of Linear Thermal Expansion X10-5 per F  2.59

 

 

 

Products    |     Product Options    |     Services    |     Case Studies    |     About Us    |     Industries    |     Connect With Us    |     Technical Resources

The Electrodyne Company, Inc.    |     4188 Taylor Road    |     Batavia, OH 45103    |     PH: 513-732-2822    |     FAX: 531-732-6953

© 2013 The Electrodyne Company, Inc., All Rights Reserved